Tus cov xov > Khoom > Iron powder > txiv qhov rooj atomized > iron powder nrog powder metallurgy
• Ni: 3.98 %
• Mo: 0.50 %
• Apparent density: 3.03 g/cm3
• Tswv rau: 25.60 S\/50g
• Tsawg ntsuav 600Mpa: 7.05 g\/cm3
• Txhais cov xovxwm: 100 mesh
LAP100.29A3 yog peb caug mus rau hauv txhais ntawm PM forging parts thiab high strength sintered machine tawb ntsig.
Pre-alloyed powders lawv nrog hauv nyob qhia tswj kev muaj 0.85% Mo thiab 1.5% Mo yog mus los yog sib ntsiab ntawm cuam cov nyob rau daim ntawv thiab nickel los sis tau noj nrog li cas teb chaw thiab covx.
Los yog compressibility nrog atomized iron powder yuav tsum ua hauv ib tug choj noj rau hauv pure iron los yog iron alloy parts nrog high tensile strength thiab high compressive strength. Atomized iron powder nrog water yuav muaj zoo los yog powder metallurgy nrog production nrog high strength machine parts. Atomized iron powder nrog water yuav muaj zoo los yog mixed rau hauv graphite, nickel powder, copper powder thiab metal powders kes yog muaj specific properties rau hauv lub final product. Yog yuav muaj zoo los yog mixed rau hauv lubricant kes yog muaj zinc stearate los yog compaction.
Kev txiav nrog Atomized iron powder LAP100.29A3
| Kev caij ntawv (%). | Chav tsev | Specification | |
| Min | Max | ||
| C | % | 0.01 | |
| Si | % | 0.05 | |
| Mn | % | 0.15 | |
| P | % | 0.020 | |
| S | % | 0.015 | |
| Ni | % | 3.80 | 4.20 |
| Mo | % | 0.40 | 0.60 |
| Tsis cov xovxwm physical | |||
| Apparent density | g/cm3 | 2.90 | 3.15 |
| Tsis rau hauv lub cas | s\/50g | 28.00 | |
| Tsib ntawv 600Mpa | g/cm3 | 6.75 | |
| Kev muaj tebchaws thiab (%). | |||
| 180-212um | % | 1 | |
| 150-180um | % | 10 | |
| 45-150um | % | ||
| -45um | % | 10 | 30 |
PRODUCT PACKING
25kg/txhab, 1000kg/txhab, cov phej yog mus ib tug xyoo rau hauv lub nyob yeej kawm.